| CDA | ASTM | SAE | AMS | Federal | Military | Other |
|---|---|---|---|---|---|---|
| C14500 | B124 B124M B301 B301M |
J461 J463 |
Tellurium-bearing (PTE) |
| Cu%1,2 | P% | Te% | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Chemical composition according to ASTM B301/B301M-13(2020)
1Includes silver 2Includes tellurium and phosphorus
Note: includes oxygen-free or deoxidized grades with deoxidizers (such as phosphorus, boron, lithium, or other) in an amount agreed upon. Unless otherwise noted, single values represent maximums.
|
|||||||||||
| 99.90 min |
0.004- 0.012 |
0.40- 0.70 |
|||||||||
| Tensile strength, min | Yield strength, at 0.5% extension under load, min | Elongation, 4x diameter or specimen thickness, min | Brinell hardness (500 kg load) | Remarks | ||
|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | % | typical BHN | |
| 38 | 260 | 30 | 205 | 8 | 76 | |
| Tensile strength, min | Yield strength, at 0.5% extension under load, min | Elongation, 4x diameter or specimen thickness, min | Brinell hardness (500 kg load) | Remarks | ||
|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | % | typical BHN | |
| 38 | 260 | 30 | 205 | 12 | 76 | |
| Tensile strength, min | Yield strength, at 0.5% extension under load, min | Elongation, 4x diameter or specimen thickness, min | Brinell hardness (500 kg load) | Remarks | ||
|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | % | typical BHN | |
| 48 | 330 | 40 | 275 | 4 | 81 | |
| Tensile strength, min | Yield strength, at 0.5% extension under load, min | Elongation, 4x diameter or specimen thickness, min | Brinell hardness (500 kg load) | Remarks | ||
|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | % | typical BHN | |
| 44 | 305 | 38 | 260 | 8 | 81 | |
| Tensile strength, min | Yield strength, at 0.5% extension under load, min | Elongation, 4x diameter or specimen thickness, min | Brinell hardness (500 kg load) | Remarks | ||
|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | % | typical BHN | |
| 40 | 275 | 35 | 240 | 8 | 81 | |
| US Customary | Metric | |
|---|---|---|
| Melting point - liquidus | 1976 °F | 1080 °C |
| Melting point - solidus | 1924 °F | 1051 °C |
| Density | 0.323 lb/in3 at 68 °F | 8.94 gm/cm3 at 20 °C |
| Specific gravity | 8.94 | 8.94 |
| Electrical conductivity | 93% IACS at 68 °F | 0.539 MegaSiemens/cm at 20 °C |
| Thermal conductivity | 205 Btu/sq ft/ft hr/°F at 68 °F | 355 W/m at 20 °C |
| Coefficient of thermal expansion 68-212 | 9.5 · 10-6 per °F (68-212 °F) | 16.5 · 10-6 per °C (20-100 °C) |
| Coefficient of thermal expansion 68-392 | 9.7 · 10-6 per °F (68-392 °F) | 16.8 · 10-6 per °C (20-200 °C) |
| Coefficient of thermal expansion 68-572 | 9.9 · 10-6 per °F (68-572 °F) | 17.1 · 10-6 per °C (20-300 °C) |
| Specific heat capacity | 0.092 Btu/lb/°F at 68 °F | 385.5 J/kg at 20 °C |
| Modulus of elasticity in tension | 17000 ksi | 117212 MPa |
| Modulus of rigidity | 6400 ksi | 44127 MPa |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene welding | Fair |
| Gas shielded arc welding | Fair |
| Coated metal arc welding | Not recommended |
| Spot weld | Not recommended |
| Seam weld | Not recommended |
| Butt weld | Fair |
| Capacity for being cold worked | Good |
| Capacity for being hot formed | Good |
| Forgeability rating | 65 |
| Machinability rating | 85 |
| Treatment | Minimum* | Maximum* |
|---|---|---|
| Annealing | 800 | 1200 |
| Hot treatment | 1400 | 1600 |
| C14500 rod | rod |
| C14500 flat bar | flat bar |
| C14500 hex bar | hex bar |
| C14500 square bar | square bar |
| C14500 rectangular bar | rectangular bar |
| C14500 shaft | shaft |
| C14500 billet | billet |
| C14500 polished bar | polished bar |
| C14500 cold drawn bars | cold drawn bars |
| C14500 annealed bars | annealed bars |
| C14500 cold finished round bars | cold finished round bars |
| C14500 forged round bars | forged round bars |
| C14500 hot rolled bars | hot rolled bars |
| C14500 Round Bar | Round Bar |
| C14500 Wire | Wire |
| C14500 Sheet | Sheet |
| C14500 Plate | Plate |
| C14500 Strips | Strips |
| C14500 Foil | Foil |
| C14500 Shims | Shims |
| C14500 Coil | Coil |
| C14500 Pipe | Pipe |
| C14500 Tubes | Tubes |
| C14500 | |
| CuTe rod | |
| CuTe flat bar | |
| CuTe hex bar | |
| CuTe square bar | |
| CuTe rectangular bar | |
| CuTe shaft | |
| CuTe billet | |
| CuTe polished bar | |
| CuTe cold drawn bars | |
| CuTe annealed bars | |
| CuTe cold finished round bars | |
| CuTe forged round bars | |
| CuTe hot rolled bars | |
| CuTe Round Bar | |
| CuTe Wire | |
| CuTe Sheet | |
| CuTe Plate | |
| CuTe Strips | |
| CuTe Foil | |
| CuTe Shims | |
| CuTe Coil | |
| CuTe Pipe | |
| CuTe Tubes | |
| CuTe |